If the kiln doesn't overshoot, and it goes through all its steps as you told it, then I reckon that sounds ok.
The first two ramps are simply to take it up to the right temperature without going too fast. The third ramp you have there is to cool the kiln down slowly- you have got it cooling down at (ramp 3) 78c per hour. That's pretty slow, but probably very good for your beads!
Looking forward to seeing your beads!

[bubblefizz]

what do you set your 3rd ramp at? im intrigued 

[*rowanberry*]

you think thats slower, mines even slower, lol.... and i have a soak at strain point.
But i do make HUGE beads!